Description
- Product Name: AG021
- Product grade: Injection molding grade
- Product features: 50% glass fiber reinforced nylon 66
- Product color: Natural color
- AG021 is a 50% glass-fiber reinforced PA for injection molding.
- Product application: Sports equipment, Shock absorber support seats, etc.
Typical molding process
| Dry | Drum wind oven: 100～120℃, 4～6h；Cycling warm air: 100～120℃,4～6h；Vacuum drying oven： 100～120℃,3～4h； |
| Processing temperrature | Feed section：275～285℃Compressing section：285～295℃Metering secion：295～300℃ |
| Injection pressure | 70～130MPa |
| Packing pressure | 40～90 MPa |
| Mold temperature | 80～120℃ |
| Back pressure | 8～15MPa |
Parameter
| Test Item | Test Standard | Test Condition | Unite | Value |
| Others | ||||
| Product Identification | ISO1043 | —— | —— | PA66-GF50 |
| Filler Content | ISO3451-1 | —— | % | 50 |
| Density | ISO1183 | 23℃ | g/cm³ | 1.57 |
| Molding shrinkage(parallel/ normal) | ISO 294-4 | —— | % | 0.3/0.7 |
| Melt Flow Rate | ISO 1133 | 275℃，2.16kg | g/10min | / |
| Mechanical | ||||
| Flexural Strength | ISO178 | 23℃，2mm/min | MPa | 275 |
| Flexural Modulus | ISO178 | 23℃，2mm/min | MPa | 12000 |
| Tensile Strength | ISO527 | Type I spline,50mm/min | MPa | 210 |
| Tensile Module | ISO527 | Type I spline,1mm/min | MPa | —— |
| Charpy Notched Impact Strength | ISO179/1eA | 23℃ | kJ/m2 | 12/C |
| Charpy Unnotched Impact Strength | ISO179/1eU | 23℃ | kJ/m2 | 75/C |
| Thermal | ||||
| Melting Temperature | ISO11357 | —— | ℃ | 260 |
| Heat Distortion Temperature | ISO75-2 | 0.45MPa | ℃ | —— |
| 1.8MPa | ℃ | —— | ||
| Flammability | ||||
| Flammability | UL-94 | 1.6mm | Class | HB |
All is typical data, only for reference, not the permit of quality assurance.