Description
- Product Name: PA6-GF10
- Product grade: Injection molding grade
- Product Features: 10% glass fiber reinforced nylon 6, meeting ROHS requirements.
- Product color: Black
- BG212 is a 10% glass-fiber reinforced PA6 .
- Product applications: Electrical terminals, socket, etc.
Typical molding process
| Dry | Drum wind oven： 100～120℃，4～6h；Cycling warm air： 100～120℃，4～6h；Vacuum drying oven： 100～120℃，3～4h； |
| Processing temperrature | Feed section：225～240℃Compressing section：250～280℃Metering secion：250～280℃ |
| Injection pressure | 50～100MPa |
| Packing pressure | 30～70 Mpa |
| Mold temperature | 60～90℃ |
| Back pressure | 0～5Mpa |
Parameter
| Test Item | Test Standard | Test Condition | Unit | Value |
| Others | ||||
| Product Identification | ISO1043 | —— | —— | PA6-GF10 |
| Filler Content | ISO3451-1 | —— | % | 10 |
| Density | ISO1183 | 23℃ | g/cm³ | 1.18 |
| Molding shrinkage(parallel/ normal) | ISO 294-4 | —— | % | 0.4/1.0 |
| Melt Flow Rate | ISO 1133 | 250℃，2.16kg | g/10min | 16 |
| Viscosity number | ISO307 | 96%H2SO4,0.5g/dl | ml/g | / |
| Mechanical | ||||
| Flexural Strength | ISO178 | 23℃，2mm/min | MPa | 130 |
| Flexural Modulus | ISO178 | 23℃，2mm/min | MPa | 3300 |
| Tensile Strength | ISO527 | Type I spline,50mm/min | MPa | 90 |
| Tensile Module | ISO527 | Type I spline,1mm/min | MPa | / |
| Tensile Strain at Break | ISO527 | Type I spline,50mm/min | % | 2.8 |
| Charpy Notched Impact Strength | ISO179/1eA | 23℃ | kJ/m2 | 8/C |
| Charpy Unnotched Impact Strength | ISO179/1eU | 23℃ | kJ/m2 | 65/C |
| Thermal | ||||
| Melting Temperature | ISO11357 | —— | ℃ | 220 |
| Heat Distortion Temperature | ISO75-2 | 0.45MPa | ℃ | / |
| 1.8MPa | ℃ | / | ||
| Electrical | ||||
| Volume Resistivity | IEC60093 | —— | Ω•cm | 1015 |
| Surface resistivity | IEC60093 | —— | Ω | 1012 |
| Flammability | ||||
| Flammability | UL-94 | 1.6mm | Class | / |
All is typical data, only for reference, not the permit of quality assurance.