Description
Product Name: BG3LT22
Product grade: Injection molding grade
Product features: 15% glass fiber reinforced toughened nylon 6, meeting ROHS requirements.
Product color: Black
Product applications: Auto parts.
Typical molding process
| Dry | Drum wind oven： 100～120℃，4～6h；Cycling warm air： 100～120℃，4～6h；Vacuum drying oven： 100～120℃，3～4h； |
| Processing temperrature | Feed section：250～270℃Compressing section：275～295℃Metering secion：265～285℃ |
| Injection pressure | 70～130MPa |
| Packing pressure | 40～90 MPa |
| Mold temperature | 80～120℃ |
| Back pressure | 8～15MPa |
Parameter
| Test Item | Test Standard | Test Condition | Unite | Value |
| Others | ||||
| Product Identification | ISO1043 | —— | —— | BG3LT22 |
| Filler Content | ISO3451-1 | —— | % | 15 |
| Density | ISO1183 | 23℃ | g/cm³ | 1.20±0.03 |
| Molding shrinkage(parallel/ normal) | ISO 294-4 | —— | % | 0.3/0.8 |
| Melt Flow Rate | ISO 1133 | 275℃，2.16kg | g/10min | 15 |
| Mechanical | ||||
| Flexural Strength | ISO178 | 23℃，2mm/min | MPa | 125 |
| Flexural Modulus | ISO178 | 23℃，2mm/min | MPa | 3300 |
| Tensile Strength | ISO527 | Type I spline,50mm/min | MPa | 87 |
| Tensile Module | ISO527 | Type I spline,1mm/min | MPa | / |
| Tensile Strain at Break | ISO527 | Type I spline,50mm/min | % | / |
| Charpy Notched Impact Strength | ISO179/1eA | 23℃ | kJ/m2 | 5 |
| Charpy Unnotched Impact Strength | ISO179/1eU | 23℃ | kJ/m2 | 40 |
| Thermal | ||||
| Melting Temperature | ISO11357 | —— | ℃ | 220 |
| Heat Distortion Temperature | ISO75-2 | 0.45MPa | ℃ | 190 |
| 1.8MPa | ℃ | 160 | ||
| Electrical | ||||
| CTI | IEC60112 | A | V | / |
| Volume Resistivity | IEC60093 | —— | Ω•cm | 1013 |
| Surface resistivity | IEC60093 | —— | Ω | 1012 |
| Flammability | ||||
| Flammability | UL-94 | 1.6mm | Class | / |
All is typical data, only for reference, not the permit of quality assurance.