Description
- Product Name: PA6-(GF10+M20)
- Product grade: Injection molding grade
- Product features: 10% glass fiber reinforced nylon 6, 20% mineral filling, resistant to low-temperature impact, low warpage deformation, excellent surface finish, and good fluidity facilitates molding.
- Product color: Black
- Product applications: Automobile engine cover、automotive parts, etc.
Typical molding process
| Dry | Drum wind oven： 100～120℃，4～6h；Cycling warm air： 100～120℃，4～6h；Vacuum drying oven： 100～120℃，3～4h； |
| Processing temperrature | Feed section：225～240℃Compressing section：245～275℃Metering secion：240～270℃ |
| Injection pressure | 70～130MPa |
| Packing pressure | 40～90 MPa |
| Mold temperature | 70～100℃ |
| Back pressure | 8～15MPa |
Parameter
| Test Item | Test Standard | Test Condition | Unite | Value |
| Others | ||||
| Product identification | ISO1043 | —— | —— | PA6-(GF10+M20) |
| Filler Content | ISO3451-1 | —— | % | 30 |
| Density | ISO1183 | 23℃ | g/cm³ | 1.35 |
| Molding shrinkage(parallel/ normal) | ISO 294-4 | —— | % | 0.4/0.6 |
| Melt Flow Rate | ISO 1133 | 250℃，2.16kg | g/10min | 20 |
| Mechanical | ||||
| Flexural Strength | ISO178 | 23℃，2mm/min | MPa | 150 |
| Flexural Modulus | ISO178 | 23℃，2mm/min | MPa | 5000 |
| Tensile Strength | ISO527 | Type I spline,50mm/min | MPa | 110 |
| Tensile Module | ISO527 | Type I spline,1mm/min | MPa | 6500 |
| Tensile Modulus | ISO527 | Humidifying,1mm/min | MPa | 3200 |
| Tensile Strain at Break | ISO527 | Type I spline,50mm/min | % | 7 |
| Charpy Notched Impact Strength | ISO179/1eA | 23℃ | kJ/m2 | 7.5 |
| Charpy Unnotched Impact Strength | ISO179/1eU | 23℃ | kJ/m2 | 50 |
| Thermal | ||||
| Melting Temperature | ISO11357 | —— | ℃ | 220 |
| Heat Distortion Temperature | ISO75-2 | 0.45MPa | ℃ | 210 |
| 1.8MPa | ℃ | 185 | ||
| Electrical | ||||
| CTI | IEC60112 | A | V | / |
| Volume Resistivity | IEC60093 | —— | Ω•cm | 1013 |
| Surface resistivity | IEC60093 | —— | Ω | 1010 |
| Flammability | ||||
| Flammability | UL-94 | 1.6mm | Class | HB |
All is typical data, only for reference, not the permit of quality assurance.