Description
- Product Name: BM6SI02
- Product grade: Injection molding grade
- Product features: 30% mineral-filled reinforced nylon 6, with excellent surface finish.
- Product color: Black
- BM6SI02 is a 30% mineral fill reinforced PA6 for injection molding, it provides prominent surface finish, in addition to providing good mechanical properties.
- Product applications: Hub cap, etc.
Typical molding process
| Dry | Drum wind oven: 100～120℃, 4～6h；Cycling warm air: 100～120℃,4～6h；Vacuum drying oven： 100～120℃,3～4h； |
| Processing temperrature | Feed section：225～240℃Compressing section：240～270℃Metering secion：240～270℃ |
| Injection pressure | 70～130MPa |
| Packing pressure | 40～90 Mpa |
| Mold temperature | 70～100℃ |
| Back pressure | 5～10Mpa |
Parameter
| Test Item | Test Standard | Test Condition | Unite | Value |
| Others | ||||
| Ash Content | ISO3451-1 | 620℃ | % | 30 |
| Melt Index | ISO1133 | 250℃，2.16kg | g/10min | 25 |
| Density | ISO1183 | 23℃ | g/cm³ | 1.31 |
| Mechanical | ||||
| Flexural Strength | ISO178 | 23℃，2mm/min | MPa | 120 |
| Flexural Modulus | ISO178 | 23℃，2mm/min | MPa | 5300 |
| Tensile Strength | ISO527 | Type I spline,50mm/min | MPa | 90 |
| Elongation at Break | ISO527 | Type I spline,50mm/min | % | 6.5 |
| Charpy Notched Impact Strength | ISO179/1eA | 23℃ | kJ/m2 | 7.5 |
| Charpy Unnotched Impact Strength | ISO179/1eU | 23℃ | kJ/m2 | 55 |
| Thermal | ||||
| Temperature of Deflection Under Load | ISO75-2 | 0.45MPa | ℃ | 205 |
| 1.8MPa | ℃ | 190 | ||
| Flammability | ||||
| Flammability | UL-94 | 1.6mm | —— | HB |